Leqephe le thata la PVC(UV e tsitsitse)

Tlhaloso e Khutšoanyane:

Boholo:
Botenya: 1mm ~ 30mm
Bophara: 1mm ~ 3mm: 1000mm ~ 1300mm
4mm ~ 20mm: 1000mm ~ 1500mm
25mm ~ 30mm: 1000mm ~ 1300mm
35mm ~ 50mm: 1000mm
Bolelele: Bolelele bofe kapa bofe.
Mefuta e tloaelehileng: 1220mmx2440mm; 1000mmx2000mm; 1500mmx3000mm.
Mebala e Tloaelehileng: Boputsoa bo lefifi (RAL7011), bohlooho bo bobebe, botšo, bosoeu, boputsoa, botala, bokhubelu le mebala efe kapa efe ho latela litlhoko tsa bareki.
Bokaholimo: E benyang, matt, e hatisitsoeng.

TS'ELISO HONA theolela faele ho pdf

Lintlha

Li-tag

Lintlha tsa tekheniki bakeng sa lakane e thata ea PVC ea UV e tsitsitse:

	Maemo a Teko (GB/T 22789.1-2008)	Yuniti	Boleng bo Tlwaelehileng
Ea nama
Botenya	1.45~1.5	g/cm³	1.45
Mechini
Tensile Strength (Bolelele/Bophara)	≥45	Mpa	52.9/48.9
Elongation (Bolelele/Bophara)	≥8	%	29/32
Notch Impact Strength (Bolelele/Bophara)	≥5	KJ/㎡	7.83/7.57
Charpy Unnotched Impact Matla0℃-20℃	—– —–	KJ/㎡ KJ/㎡	pendulum 4J Mohlala ha o robehe
Matla a ho Kobela V=2mm/min	—–	Mpa	76.2
Ball Indentation Hardness 358N(h: 0.118~0.138)	—–	N/m㎡	221
Mocheso
Vicat Softening Temperature	≥70	°C	76.8
Ho Shrinkage ha Mocheso (Bolelele/Bophara)	-4~+4	%	+1.9/-0.1
Mocheso oa ho kheloha tlas'a mojaro (Bolelele / Bophara)	—–	°C	69.5/69.7
Lik'hemik'hale
35% ±1% (v/v) HCI 5h 60°C	±10	g/cm3	+5
30%±1% (v/v) H2SO4 5h 60°C	±8	g/cm3	+4
40%±1% (v/v) HNO3 5h 60°C	±8	g/cm3	+4
40%±1% (v/v) NaOH 5h 60°C	±5	g/cm3	+2
Motlakase
Ho hanyetsa Molumo	—–	ohm·cm	5.5×10¹³

Lisebelisoa:
Lipampiri tse thata tsa PVC tsa UV tse tsitsitseng li sebelisoa haholo indastering e akaretsang le ea lik'hemik'hale, joalo ka lisebelisoa tsa Lab, lisebelisoa tsa Etching, lisebelisoa tsa ho sebetsa tsa semiconductor, libarele tsa ho roala, tanka ea metsi, tanka ea polokelo ea lik'hemik'hale, tanka ea oli, tanka ea ho boloka metsi a ritelo, tora ea tlhahiso ea acid kapa alkali. , tora ea ho hlatsoa acid kapa alkali, lisebelisoa tse hlahisang lifoto; Liindasteri tsa motlakase bakeng sa lebokose la betri, poleiti ea electrometer, tanka ea electrolytic le lipoleiti tse fapa-fapaneng tsa ho kenya motlakase, li-signboards bakeng sa papatso, marako a marako a ofisi le lisebelisoa tsa sechaba, liphanele tsa mamati joalo-joalo.

R&D:
1.Khampani ea rona e amohela lisebelisoa tse tala tse nang le tikoloho.Ho laola ka thata mokhoa oa tlhahiso, ho tloha lihlahisoa tse tala ho ea ho tlhahlobo ea boleng ba lera la fektheri.Teko ea liteko e latela tsamaiso ea boleng ba machaba le tsamaiso ea setifikeiti ho netefatsa boleng ba lihlahisoa.
2.Khampani ea rona e thehile liteko tse ngata tse ikemetseng, tse nang le tekanyo e phahameng ea ho iketsetsa lisebelisoa tsa tlhahiso, selemo se seng le se seng ho kenya chelete e ngata, ho kenngoa ha talenta le theknoloji, ho na le matla a matla a lipatlisiso tsa saense.

Haeba u thahasella lihlahisoa tsa rona, u ka khetha ho siea lintlha tsa hau mona, 'me re tla buisana le uena haufinyane.

Ngola molaetsa wa hao mona mme o re romele wona